Marine Covering Coat (HT-02)

HT-02 marine covering coat is a new product which was recently developed by our company, the base material of the product is epoxy resin, the auxiliary materials are abrasion-resisting fillers and other assistant agents, via reasonable blending, and manufactured the marine covering coat which having high performance, chemically curing and self-leveling.
HT-02 marine covering coat can be coated onto the surfaces of cement concrete, steel plates and woods, and forms the gloss or sub-gloss ground. It has characteristics of comfortable for walking, surface flexible, colorful, antiskid and abrasion-resistant, waterproof, acid-proof and alkali-resistant and good adhesion. It is applicable for use in industrial grounds, all kinds of ship decks, building grounds and the testing places which need high requirements.
Property:
Characteristic: Comfortable for walking, surface flexible, colorful, antiskid and abrasion-resistant, waterproof, acid-proof and alkali-resistant and good adhesion
Applicable for: Use for industrial grounds, all kinds of ship decks, building grounds and the testing places which need high requirements
Consume amount: 2.476 kg/m2
Packing: Base material (A component): 13.5kg/barrel; Curing agent (B component):
4.5kg/barrel; Filler (C component): 20kg/pack; Thinner: 10kg/barrel
Storage: Ventilation place, the quality guarantee period is 12 months
Approval Certificate: CCS

Application Method:
1 Preparation prior to application
1.1 The steel decks fairing by hot working, all the embedded parts installation and welding that may interfere with the application of covering are to be finished beforehand.
1.2 The oils, water, paints, rusts, dusts on the steel plates are to be removed meanwhile the surface preparation is carried out according to the requirements of Grade P2 of CB3230 or Grade St2 of ISO8501-1.
2 Application Procedures
2.1 Firstly stir the dry materials(A component) evenly in agitator, and pour the liquid (B component) into the agitator according to the specified ratio of the dry materials and liquid, stirring it about 3 minutes, and then for application immediately.
2.2 Pour the mixed covering onto the cleaned steel decks, rub the covering back and forth with a trowel to moisture the steel decks sufficiently, then striking off the covering with wooden ruler.
2.3 Consolidating and leveling the covering surface with trowel, the roughness of the surface within 2 meters shall not be over 5mm. If the covering surface is a bit too hard for leveling, should spray some latex first and then level it.
2.4 After the covering application finished, it should be kept maintain for 1 to 2 days with spray a suitable amount of water or maintaining agent on its surface, and people may walk on it after it hardened.
4.2.5 After the covering is completely hardened (about 1 to 2 weeks), the floors should be adhered.
4.2.6 In the whole application and maintenance period, the environmental temperature should be a range of 0~35º C, cool-down measure is to be taken if the temperature is higher than 35º C or heat preservation measure is to be taken if the temperature is lower than 0º C.

Attentions
The liquid (latex) shall be kept in cool place (0~35º C). If the surface of liquid has gels, the gels shall be removed, and the liquid can still be used.
The dry material shall be kept in dry place, avoid rain showering or water dipping. If the dry material is obviously caked, it shall not be used.
The mixing ratio: A component: B component = 2: 1(Pack ratio).